Craig Dworkin

Ink on a 5.5 by 9 inch substrate of 60 -pound offset matte white paper. Composed of: varnish (soy bean oil [ C 57 H 98 O 6 ], used as a plasticizer: 52 % . Phenolic modified rosin resin [Tall oil rosin: 66.2 % . Nonylphenol [ C 15 H 24 O ]: 16.6 %. Formaldehyde [ CH 2 O ]: 4.8 %. Maleic anhydride [ C 4 H 2 O 3 ]: 2.6 % . Glycerol [ C 3 H 8 O 3 ]: 9.6 % . Traces of alkali catalyst: .2 %] : 47 %): 53.7 %. 100S Type Alkyd used as a binder (Reaction product of linseed oil: 50.7 %. Isophthalic acid [ C 8 H 6 O 4 ]: 9.5 %. Trimethylolpropane [ CH 3 CH 2 C(CH 2 OH) 3 ]: 4.7 % . Reaction product of tall oil rosin: 12.5 %. Maleic anhydride [ C 4 H 2 O 3 ]: 2.5 %. Pentaerythritol [ C 5 H 12 O 4 ]: 5 %. Aliphatic C 14 Hydrocarbon: 15 %): 19.4 %. Carbon Black (C: 92.8 %. Petroleum: 5.1 %. With sulfur, chlorine, and oxygen contaminates: 2.1 %) , used as a pigmenting agent: 18.6 %. Tung oil (Eleostearic acid [ C 18 H 30 O 2 ]: 81.9 %. Linoleic acid [ C 18 H 32 O 2 ]: 8.2 % . Palmitic acid [ C 16 H 32 O 2 ]: 5.9 % . Oleic acid [ CH 3 (CH 2 ) 7 CH=CH(CH 2 ) 7 COOH ]: 4.0 %. ), used as a reducer: 3.3 % . Micronized polyethylene wax ( C 2 H 4 )N: 2.8 %. 3 / 50 Manganese compound, used as a through drier: 1.3 % . 1 / 25 Cobalt linoleate compound used as a top drier: .7 % . Residues of blanket wash (roughly equal parts aliphatic hydrocarbon and aromatic hydrocarbon): .2 % . Adhered to: cellulose [ C 6 H 10 O 5 ] from softwood sulphite pulp (Pozone Process) of White Spruce ( 65 %) and Jack Pine ( 35 %): 77 %; hardwood pulp (enzyme process pre-bleach Kraft pulp) of White Poplar (aspen): 15 %; and batch treated PCW ( 8 %): 69.3 %. Water [ H 2 O ]: 11.0 % . Clay [Kaolinite form aluminum silicate hydroxide ( Al 2 Si 2 O 5 [OH] 4 ): 86 %. Calcium carbonate ( CaCO 3 ): 12 %. Diethylenetriamine: 2 %], used as a pigmenting filler: 8.4 %. Hydrogen peroxide [ H 2 O 2 ], used as a brightening agent: 3.6 %. Rosin soap, used as a sizer: 2.7 % . Aluminum sulfate [ Al 2 (SO 4 ) ]: 1.8 % . Residues of cationic softener ( H 2 O : 83.8 %. Base [Stearic acid ( C 18 H 36 O 2 ): 53.8 % . Palmitic acid ( C 16 H 32 O 2 ): 29 % . Aminoethylethanolamine ( H 2 -NC 2 -H 4 -NHC 2 -H 4 -OH ): 17.2 %]: 10.8 % . Sucroseoxyacetate: 4.9 % . Tallow Amine, used as a surfactant: 0.3 % . Sodium chloride [ NaCl ], used as a viscosity controlling agent: .2 %) and non-ionic emulsifying defoamer (sodium salt of dioctylsulphosuccinate [ C 20 H 37 NaO 7 S ]), combined: 1.7 % . Miscellaneous foreign contaminates: 1.5 % .